Show simple item record

dc.contributor.authorJaramillo Suárez, Héctor Enriquespa
dc.contributor.authorAlba de Sánchez, Nelly Ceciliaspa
dc.contributor.authorsanchez sthepa, hectorspa
dc.contributor.authorÁvila Díaz, Julián Arnaldospa
dc.coverage.spatialUniversidad Autónoma de Occidente. Calle 25 115-85. Km 2 vía Cali-Jamundíspa
dc.date.accessioned2020-02-17T16:41:58Zspa
dc.date.available2020-02-17T16:41:58Zspa
dc.date.issued2010-10spa
dc.identifier.citationJaramillo Suárez, Héctor Enrique; Alba de Sánchez, Nelly Cecilia; Sánchez Sthepa, Héctor; Ávila Díaz, Julián Arnaldo. Synthesis and characterization of aluminum titanium carbonitride TiAlCN via mechanical alloying. En: Journal of Scientific & Industrial Research Volumen 69, (octubre 2010); páginas 773-776eng
dc.identifier.urihttp://red.uao.edu.co//handle/10614/11907spa
dc.identifier.urihttps://www.researchgate.net/publication/259763811_Synthesis_and_characterization_of_aluminum_titanium_carbonitride_TiAlCN_via_mechanical_alloyingeng
dc.description.abstractEste estudio presenta síntesis de aleación de carbonitruros de titanio y aluminio (TiAlCN) mediante aleación mecánica en molino de bolas Attritor a partir de polvos elementales de titanio, aluminio y grafito en atmósfera de nitrógeno. TiAlCN se caracterizó por técnicas SEM, XRD, DSC y FTIR. La XRD mostró presencia de nitruro de titanio aluminio, nitruro de aluminio, carburo de titanio y nitruro de carbono titanio aluminio, mientras que SEM mostró existencia de micro y nano partículas con alta aglomeración. El análisis de espectroscopía de dispersión de energía (EDS) muestra una distribución homogénea de elementos, y el análisis de mapeo de rayos X confirma la distribución de elementos. Introducción El desarrollo de la aleación ternaria Ti-Al-N aumenta la dureza y la resistencia a la oxidación en comparación con la aleación binaria TiN 1. Tipo de aleaciones cuaternarias, titanio aluminio carbonitruro de titanio (Ti-Al-NC) se ha producido mediante la técnica de deposición láser pulsada 2-3, la técnica de pulverización catódica con magnetrón 6 y las técnicas de deposición química 4. El recubrimiento duro de aleación de carbonitruros de aluminio y titanio (TiAlCN) muestra una alta resistencia al desgaste y la erosión, bajo alta velocidad de corte y sin lubricación 6. Este estudio presenta síntesis por aleación mecánica y caracterización de la aleación en polvo TiAlCN como objetivo para la obtención de recubrimientos duros. El polvo de TiAlCN de la Sección Experimental (Ti, 55,1; Al, 31,0; y C, 13,9%) se obtuvo mediante aleación mecánica en un molino de bolas en un rotor del impulsor vertical 6. Se utilizaron un vial de acero inoxidable y varias bolas de acero Cr (diámetro, 6-8 mm). Polvo elemental contenido: Ti puro (tamaño de partícula, 150 µm), 99,7% en peso; Al (tamaño de partícula, <200 µm), 99,95% en peso; y C (tamaño de partícula, <45 µm), 99,99% en peso. El aire del recipiente del molino se evacuó usando una bomba de vacío y luego se llenó con gas nitrógeno. La proporción de bolas de masa y polvo fue de 70: 1, con una velocidad de rotación constante de 500 rpm durante 140 h.spa
dc.description.abstractThis study presents synthesis of titanium aluminum carbonitrides alloy (TiAlCN) by mechanical alloying in Attritor ball mill from elemental powders of titanium, aluminum and graphite in nitrogen atmosphere. TiAlCN was characterized by SEM, XRD, DSC and FTIR techniques. XRD showed presence of titanium aluminum nitride, aluminum nitride, titanium carbide and titanium aluminum carbon nitride, while SEM showed existence of micro and nano particles with high agglomeration. Energy-dispersive spectroscopy (EDS) analysis shows a homogeneous distribution of elements, and mapping analysis from X-rays confirms distribution of elements. Introduction Development of Ti-Al-N ternary alloy gives an increase in hardness and oxidation resistance in comparison with binary alloy TiN 1 . Quaternary alloys type, titanium aluminum carbonitride titanium (Ti-Al-N-C) has been produced by pulsed laser deposition technique 2-3 , magnetron sputtering technique 6 , and chemical depositions techniques 4 . Titanium aluminum carbonitrides alloy (TiAlCN) hard coating shows high wear and erosion resistance, under high cutting velocity and without lubrication 6 . This study presents synthesis by mechanical alloying and characterization of powder alloy TiAlCN as target to obtain hard coatings. Experimental Section TiAlCN powder (Ti, 55.1; Al, 31.0; and C, 13.9%) was obtained by mechanical alloying in a ball milling atritor of vertical impeller 6 . A stainless steel vial and various Cr steel balls (diam, 6-8 mm) were used. Elemental powder contained: pure Ti (particle size, 150 µm), 99.7 wt%; Al (particle size, < 200 µm), 99.95 wt%; and C (particle size, <45 µm), 99.99 wt%. Mill container air was evacuated using a vacuum pump and then filled with nitrogen gas. Mass balls and powder ratio was 70:1, with 500 rpm constant rotational velocity for 140 h.eng
dc.formatapplication/pdfeng
dc.format.extent773-776 páginasspa
dc.language.isoengeng
dc.publisherResearchgateeng
dc.relationJournal of Scientific & Industrial Research . Volumen 69, (octubre 2010); páginas 773-776eng
dc.rightsDerechos Reservados - Universidad Autónoma de Occidentespa
dc.rights.urihttps://creativecommons.org/licenses/by-nc-nd/4.0/spa
dc.sourceinstname:Universidad Autónoma de Occidentespa
dc.sourcereponame:Repositorio Institucional UAOspa
dc.subjectCarbideseng
dc.subjectElemental powderseng
dc.subjectMechanical alloyingeng
dc.subjectNitrideseng
dc.subjectTitanium aluminum carbonitrides alloyeng
dc.titleSynthesis and characterization of aluminum titanium carbonitride TiAlCN via mechanical alloyingeng
dc.typeArtículo de revistaspa
dc.subject.armarcCarburosspa
dc.subject.armarcAleación mecánicaspa
dc.relation.referencesLai C, Cheng K, Lin S & Yeh J, Mechanical and tribological properties of multi-element (AlCrTaTiZr)N coatings, Surface Coatings Technol, 202 (2008) 3732-3738.eng
dc.relation.referencesLackner J M, Waldhauser W, Ebner R, Bakker R J, Schöberl T & Major B, Room temperature pulsed laser deposited (Ti, Al)CxN1-x coatings chemical, structural, mechanical and tribological properties, Thin Solid Films, 468 (2004) 125-133.eng
dc.relation.referencesLackner J M, Waldhauser W, Ebner R, Keckes J & Schöberl T,Room temperature deposition of (Ti,Al)N and (Ti,Al)(C,N) coatings by pulsed laser deposition for tribological applications, Surface Coatings Technol, 177-178 (2004) 447-452.eng
dc.relation.referencesShieh J & Hon M H, Observation of plastic deformation in TiAlCN/a-C ceramic nanocomposite coating, Appl Phys, A80 (2005) 131-134.eng
dc.relation.referencesZhang X, Jiang J, Yuqiao Z, Lin J, Wang F & Moore J J, Effect of carbon on TiAlCN coatings deposited by reactive magnetron sputtering, Surface Coatings Technol, 203 (2008) 594-597.eng
dc.relation.referencesTorres A F, Torres J G, Jaramillo H E, de Sánchez N A & Sánchez H, Obtención de blancos de carburo de titanio TiC mediante aleamiento mecánico, Suplemento de la Revista Latinoamericana de Metalurgia y Materiales, S1 (2009) 851-855.eng
dc.relation.referencesCastañeda J P & Martínez P, Evaluación de la tensión,elongación y temperatura de transición vítrea en los termoplásticos obtenidos a partir de almidones nativos de achira y cidra papa mediante el método “casting”, Undergraduate Thesis, Universidad del Cauca, Facultad de Ciencias Agropecuarias, Popayán, Colombia, 2009.eng
dc.relation.referencesRosliza R, WanNik W B, Izman S & Prawoto Y, Anti-corrosive properties of natural honey on Al–Mg–Si alloy in sea water, Currt Appli Phys 10 (2010) 923-929.eng
dc.relation.referencesYate L, Aperador W, Caicedo J C, Espinoza F J, Zambrano G & Muñoz J, Efecto del Voltaje Bias D.C. en las propiedades electroquímicas de películas delgadas de AlN obtenidas por Medio de la técnica Magnetrón Sputtering RF, Revista Colombiana de Física 41 (2009) 40-42.eng
dc.relation.referencesAlba N C, Producción, caracterización y optimización de recubrimientos de nitruro de carbono CNx , Ph D Thesis,Universidad del Valle, Departamento de Física, Cali,Colombia, 2002.eng
dc.rights.accessrightsinfo:eu-repo/semantics/openAccessspa
dc.rights.creativecommonsAtribución-NoComercial-SinDerivadas 4.0 Internacional (CC BY-NC-ND 4.0)spa
dc.type.coarhttp://purl.org/coar/resource_type/c_6501spa
dc.type.contentTextspa
dc.type.driverinfo:eu-repo/semantics/articlespa
dc.type.redcolhttp://purl.org/redcol/resource_type/ARTREFspa
oaire.accessrightshttp://purl.org/coar/access_right/c_abf2spa
oaire.versionhttp://purl.org/coar/version/c_970fb48d4fbd8a85spa
dc.type.versioninfo:eu-repo/semantics/publishedVersionspa


Files in this item

Thumbnail
Thumbnail

This item appears in the following Collection(s)

Show simple item record

Derechos Reservados - Universidad Autónoma de Occidente
Except where otherwise noted, this item's license is described as Derechos Reservados - Universidad Autónoma de Occidente